The failure of any welded joint is at best inconvenient and at worst can lead to catastrophic accidents. Fracture and fatigue of welded joints and structures analyses the processes and causes of fracture and fatigue, focusing on how the failure of welded joints and structures can be predicted and minimised in the design process. Part one concentrates on analysing fracture of welded joints and structures, with chapters on constraint-based fracture mechanics for predicting joint failure, fracture assessment methods and the use of fracture mechanics in the fatigue analysis of welded joints. In part two, the emphasis shifts to fatigue, and chapters focus on a variety of aspects of fatigue analysis including assessment of local stresses in welded joints, fatigue design rules for welded structures, k-nodes for offshore structures and modelling residual stresses in predicting the service life of structures. With its distinguished editor and international team of contributors, Fracture and fatigue of welded joints and structures is an essential reference for mechanical, structural and welding engineers, as well as those in the academic sector with a research interest in the field. Analyses the processes and causes of fracture and fatigue, focusing predicting and minimising the failure of welded joints in the design process Assesses the fracture of welded joints and structure featuring constraint-based fracture mechanics for predicting joint failure Explores specific considerations in fatigue analysis including the assessment of local stresses in welded joints and fatigue design rules for welded structures

This book provides a basis for the design and analysis of welded components that are subjected to fluctuating forces, to avoid failure by fatigue. It is also a valuable resource for those on boards or commissions who are establishing fatigue design codes. For maximum benefit, readers should already have a working knowledge of the basics of fatigue and fracture mechanics. The purpose of designing a structure taking into consideration the limit state for fatigue damage is to ensure that the performance is satisfactory during the design life and that the survival probability is acceptable. The latter is achieved by the use of appropriate partial safety factors. This document has been prepared as the result of an initiative by Commissions XIII and XV of the International Institute of Welding (IIW).

Local approaches to fatigue assessment are used to predict the structural durability of welded joints, to optimise their design and to evaluate unforeseen joint failures. This standard work provides a systematic survey of the principles and practical applications of the various methods. It covers the hot spot structural stress approach to fatigue in general, the notch stress and notch strain approach to crack initiation and the fracture mechanics approach to crack propagation. Seam-welded and spot-welded joints in structural steels and aluminium alloys are also considered.This completely reworked second edition takes into account the tremendous progress in understanding and applying local approaches which has been achieved in the last decade. It is a standard reference for designers, structural analysts and testing engineers who are responsible for the fatigue-resistant in-service behaviour of welded structures. Completely reworked second edition of a standard work providing a systematic survey of the principles and practical applications of the various methods Covers the hot spot structural stress approach to fatigue in general, the notch stress and notch strain approach to crack initiation and the fracture mechanics approach to crack propagation. Written by a distinguished team of authors

The key to avoidance of fatigue, which is the main cause of service failures, is good design. In the case of welded joints, which are particularly susceptible to fatigue, design rules are available. However, their effective use requires a good understanding of fatigue and an appreciation of problems concerned with their practical application. Fatigue strength of welded structures has incorporates up-to-date design rules with high academic standards whilst still achieving a practical approach to the subject. The book presents design recommendations which are based largely on those contained in recent British standards and explains how they are applied in practice. Attention is also focused on the relevant aspects of fatigue in welded joints which are not yet incorporated in codes thus providing a comprehensive aid for engineers concerned with the design or assessment of welded components or structures. Background information is given on the fatigue lives of welded joints which will enable the engineer or student to appreciate why there is such a contrast between welded and unwelded parts, why some welded joints perform better than others and how joints can be selected to optimise fatigue performance.

The Welding Engineer's Guide to Fracture and Fatigue provides an essential introduction to fracture and fatigue and the assessment of these failure modes, through to the level of knowledge that would be expected of a qualified welding engineer. Part one covers the basic principles of weld fracture and fatigue. It begins with a review of the design of engineered structures, provides descriptions of typical welding defects and how these defects behave in structures undergoing static and cyclical loading, and explains the range of failure modes. Part two then explains how to detect and assess defects using fitness for service assessment procedures. Throughout, the book assumes no prior knowledge and explains concepts from first principles. Covers the basic principles of weld fracture and fatigue. Reviews the design of engineered structures, provides descriptions of typical welding defects and how these defects behave in structures undergoing static and cyclical loading, and explains the range of failure modes. Explains how to detect and assess defects using fitness for service assessment procedures.

These recommendations present general methods for the assessment of fatigue damage in welded components, which may affect the limit states of a structure, such as ultimate limit state and serviceability limited state. Fatigue resistance data is given for welded components made of wrought or extruded products of ferritic/pearlitic or banitic structural steels up to fy = 700 Mpa and of aluminium alloys commonly used for welded structures.